The linear expansion rate of magnesia bricks at 1000-1600℃ is generally 1.0%-2.0% and it is approximate or linear. Among refractory products the thermal conductivity of magnesia is second only to carbon-containing bricks which increases with the inc
Keywords:
Category:
Refractory Fire Brick
E-mail:
154872569@qq.com
Magnesite Brick Details
The linear expansion rate of magnesia bricks at 1000-1600℃ is generally 1.0%-2.0%, and it is approximate or linear. Among refractory products, the thermal conductivity of magnesia is second only to carbon-containing bricks, which increases with the increase of temperature. reduce. Under the condition of 1100 ℃ water cooling, the number of thermal shocks is only 1 to 2 times. It has strong resistance to alkaline slag of CaO and ferrite, but weak resistance to acidic slag containing SiO2, so it cannot be in direct contact with silica bricks during use, and is generally separated by neutral bricks.
Features
1.High refractoriness. The refractoriness of magnesia brick is above 2000 degrees.
2.The softening temperature under load is high. The softening temperature under load is between 1500-1550 degrees.
3.Slag resistance. Strong resistance to alkaline slag such as CAO and FEO.
4.Thermal shock resistance. Can withstand 2-8 times
5.High temperature volume stability. The linear expansion coefficient of magnesia brick is large, and the volume stability at high temperature is poor, so enough expansion joints should be left during masonry.
Applications
Magnesia bricks are widely used in steelmaking furnace linings, ferroalloy furnaces, iron mixing furnaces, non-ferrous metallurgical industry furnaces, lime kilns for building materials, and glass industry regenerator lattices due to their good high temperature performance and strong resistance to alkaline slag. Heat exchangers, high temperature calcining kilns and tunnel kilns in the refractory industry, etc.
Physical And Chemical Indicators
Brand Properties |
MD92 |
MD95 |
MD97 |
MD98 |
|
Bulk density(g/cm3) |
2.90 |
2.95 |
3.00 |
3.00 |
|
Refractoriness under load T2 (ºC) |
1550 |
1650 |
1700 |
1700 |
|
Apparent Porosity (%) |
18 |
16 |
15 |
15 |
|
Cold Crushing Strength(MPa) |
55 |
60 |
70 |
80 |
|
Thermal shock resistance 950deg air cool (times) |
10 |
10 |
10 |
10 |
|
Composition(%) |
MGO |
92 |
95 |
97 |
97.5 |
CaO |
2.5 |
2.0 |
1.6 |
1.2 |
|
SiO2 |
3.5 |
2.5 |
1.2 |
0.6 |
Semi-silica brick refers to an aluminum-silicon refractory product with a SiO2 content of greater than 65% and an Al2O3 content of 15% to 30%. They generally use clay containing quartz impurities or native kaolin refractory clay or tailings and pyroph...
The Al2O3 content of anchor bricks is above 55%, and some users require that the alumina content reach 75%, and the load softening temperature of 75% bricks reaches 1550C. However, in actual use, anchor bricks with high aluminum content cannot be enough. The key is Flexibility is the most important t...
Products Desc
Products Description The main components of alkali resistant bricks are clay, high alumina, quartz sand, bauxite and other alkali resistant materials, among which quartz sand and bauxite can improve alkali resistance, clay and high alumina can increase sintering pressure, so that alkali-resistant bri...
Professional solutions for you, ready for your choice
Copyright © Zibo Lifa Refractory Materials Factory ALL RIGHTS RESERVED
Technical Support: JinZhao E-commerce