Al 2 O 3 SiC C brick is made from high-grade bauxite, fused alumina, silicon carbide and graphite as raw materials and resin as binder. It features excellent corrosion and erosion resistance and thermal shock resistance, and have high refractoriness under load. Al 2 O 3 SiC C brick refers to the non-burnt carbon composite refractory material that uses AL2O3, SiC and carbon raw materials as the main components and synthetic phenolic resin as the binder. The production of Al 2 O 3 SiC C mainly includes fused corundum, sintered corundum, alumina clinker, andalusite, silicon carbide, graphite and o
Keywords:
Category:
Shape Refractory
E-mail:
154872569@qq.com
Al2O3 SiC C Brick Details
Al2O3 SiC C brick is made from high-grade bauxite, fused alumina, silicon carbide and graphite as raw materials and resin as binder. It features excellent corrosion and erosion resistance and thermal shock resistance, and have high refractoriness under load.
Al2O3 SiC C brick refers to the non-burnt carbon composite refractory material that uses AL2O3, SiC and carbon raw materials as the main components and synthetic phenolic resin as the binder. The production of Al2O3 SiC C mainly includes fused corundum, sintered corundum, alumina clinker, andalusite, silicon carbide, graphite and other additives. In addition, a certain amount of fused magnesia is added to the matrix, so that the brick forms spinel during the application process, and has residual expansion properties, and improves the thermal strength, thereby enhancing the brick's corrosion resistance.It is mainly used for lining of hot metal pretreatment equipment such as torpedo-type mixed iron trucks and hot metal tanks. AL2O3 SiC C brick has excellent slag resistance and thermal shock resistance, as well as good erosion resistance and wear resistance. It is by far the most ideal lining material on hot metal pretreatment containers.
Production Process:
Adding carbon raw materials to the main alumina raw materials, adding a small amount of other raw materials such as silicon powder, SiC powder, aluminum powder, etc., using phenolic resin or asphalt as a binder, after batching, mixing , Isostatic pressing (or machine pressing), firing in a reducing atmosphere.
Features
High refractoriness.
Good spalling resistance and wear resistance.
Good corrosion resistance.
Good thermal shock resistance.
High mechanical strength.
High-temperature creep rate is low.
Applications
Mainly used in pig iron ladle furnace,steel oxidation conversion furnace lining and tapping hole, high power electric furnace wall hot place, and outside the furnace refining furnace lining, ladle slag line parts and so on.
Specifications
Widely used throughout metallurgical industry
Physical And Chemical Indicators
Brand |
TC SZ |
TC MZ |
TC BI |
TC TR |
|
Apparent Porosity (%) |
7 |
8 |
8 |
9 |
|
Bulk Density (g/cm3) |
3.00 |
2.98 |
2.98 |
2.93 |
|
Cold Crushing Strength (MPa) |
55 |
50 |
45 |
45 |
|
Thermal Linear Expansion(%) @ 1,000℃ |
0.58 |
0.55 |
0.55 |
0.52 |
|
Refractoriness Under Load (℃) @0.2MPa |
1750 |
1700 |
1700 |
1650 |
|
Chemical Analysis (%) |
Al2O3 |
72 |
68 |
67 |
65 |
SiC |
11 |
10 |
10 |
10 |
|
FC |
13 |
12 |
11 |
10 |
|
Main Applications |
Torpedo & Iron Ladle |
Semi-silica brick refers to an aluminum-silicon refractory product with a SiO2 content of greater than 65% and an Al2O3 content of 15% to 30%. They generally use clay containing quartz impurities or native kaolin refractory clay or tailings and pyroph...
The Al2O3 content of anchor bricks is above 55%, and some users require that the alumina content reach 75%, and the load softening temperature of 75% bricks reaches 1550C. However, in actual use, anchor bricks with high aluminum content cannot be enough. The key is Flexibility is the most important t...
Products Desc
Products Description The main components of alkali resistant bricks are clay, high alumina, quartz sand, bauxite and other alkali resistant materials, among which quartz sand and bauxite can improve alkali resistance, clay and high alumina can increase sintering pressure, so that alkali-resistant bri...
Professional solutions for you, ready for your choice
Copyright © Zibo Lifa Refractory Materials Factory ALL RIGHTS RESERVED
Technical Support: JinZhao E-commerce