Insulation silica brick is a very special material, which is an acidic material with a silica content of more than 92%. It is characterized by resistance to acid slag erosion. It has high high temperature strength. Load softening start temperature is 1450~1670℃. Moreover, it will not deform for a long time under high temperature. Lightweight silica bricks do not change in crystal form above 600 C. The coefficient of expansion is small. Has high thermal shock resistance. Below 600C, the crystal transformation is very large, the volume change is large, and the thermal shock resistance becomes
Keywords:
Category:
Shape Refractory
E-mail:
154872569@qq.com
Insulation Silica Brick Details
Insulation silica brick is a very special material, which is an acidic material with a silica content of more than 92%. It is characterized by resistance to acid slag erosion. It has high high temperature strength. Load softening start temperature is 1450~1670℃. Moreover, it will not deform for a long time under high temperature.
Lightweight silica bricks do not change in crystal form above 600 °C. The coefficient of expansion is small. Has high thermal shock resistance. Below 600°C, the crystal transformation is very large, the volume change is large, and the thermal shock resistance becomes poor. Lightweight silica bricks are made of natural silica as raw material, plus mineralizers, and are slowly fired at 1350-1430°C in a reducing atmosphere.
1. The thermal conductivity is only half of that of ordinary silica bricks, and the thermal shock resistance is good
2. The starting temperature of load softening can reach 1600°C, which is much higher than that of clay insulation bricks
3. Excellent fire resistance, the highest service temperature can reach 1550°C
4. The thermal stability is better than that of dense silica bricks, and it can be used for a long time at 1500~1550°C without contact with slag
Applications
Insulation silica bricks can be applied to:
blast furnace blast part, communicated with blast furnace air extractor;
Good thermal insulation performance in the convex lower part of the glass kiln vault;
Partition walls of the carbonization chamber and combustion chamber of coke ovens, regenerators and sedimentation chambers of steelmaking open hearth furnaces, soaking furnaces, glass melting furnaces, firing kilns for refractory materials and ceramics;
Vaults and other load-bearing parts of kilns;
The high-temperature load-bearing parts of the hot blast stove and the top of the acid open hearth furnace.
Physical And Chemical Indicators
牌号Brand |
S-1.0 |
S-1.1 |
S-1.2 |
SM-1.8 |
|
Bulk Density (kg/m3) |
1 |
1.1 |
1.2 |
1.80-1.95 |
|
Cold Crushing Strength (MPa) |
3 |
4 |
5 |
20 |
|
≤ 2% Permanent Linear Change (℃) |
1450 |
1500 |
1550 |
- |
|
350℃±10℃ Thermal Conductivity(W/m.k) |
0.50 |
0.60 |
0.70 |
0.20 |
|
@T2 Refractoriness Under Load (℃) |
1400 |
1420 |
1520 |
1280 |
|
Chemical Composition(%) |
SiO₂ |
91 |
91 |
91 |
77-81 |
Semi-silica brick refers to an aluminum-silicon refractory product with a SiO2 content of greater than 65% and an Al2O3 content of 15% to 30%. They generally use clay containing quartz impurities or native kaolin refractory clay or tailings and pyroph...
The Al2O3 content of anchor bricks is above 55%, and some users require that the alumina content reach 75%, and the load softening temperature of 75% bricks reaches 1550C. However, in actual use, anchor bricks with high aluminum content cannot be enough. The key is Flexibility is the most important t...
Products Desc
Products Description The main components of alkali resistant bricks are clay, high alumina, quartz sand, bauxite and other alkali resistant materials, among which quartz sand and bauxite can improve alkali resistance, clay and high alumina can increase sintering pressure, so that alkali-resistant bri...