Magnesia Carbon Brick has excellent resistance to spalling, rust and excellent oxidation resistance. It can be used in electric furnaces, the second ladle, etc., and is widely popular in the steelmaking industry. It uses high-purity, high-density, molten large crystalline magnesium oxide and high-purity graphite as the main raw materials, adding an appropriate amount of antioxidants, and using a high-pressure molding process, using phenolic resin as a binder. This product is mainly used in the converter lining, which is in direct contact with molten steel and molten slag. It has the advantages
Keywords:
Category:
Shape Refractory
E-mail:
154872569@qq.com
Magnesia Carbon Brick Details
Magnesia Carbon Brick has excellent resistance to spalling, rust and excellent oxidation resistance. It can be used in electric furnaces, the second ladle, etc., and is widely popular in the steelmaking industry. It uses high-purity, high-density, molten large crystalline magnesium oxide and high-purity graphite as the main raw materials, adding an appropriate amount of antioxidants, and using a high-pressure molding process, using phenolic resin as a binder. This product is mainly used in the converter lining, which is in direct contact with molten steel and molten slag. It has the advantages of high strength, strong slag resistance, good thermal shock stability and high refractoriness.
Advantages
Magnesia Carbon Brick has proper residual expansion, low thermal conductivity and better insulation performance than magnesium aluminum carbon brick. The performance of magnesium aluminum carbon brick is between magnesium carbon and aluminum magnesium carbon. It belongs to high melting point basic oxide material, which has high heat resistance, strong slag resistance, good thermal shock resistance and low creep under high temperature. This brick has been used in the ladle refining slag line and has achieved good results. It is also used in the lining part of AC electric arc furnace, DC electric arc furnace, converter and other components.
Applications
Magnesia Carbon Brick has the following applications:
-EAF(Electrick arc furnace)
-Ladle
-Basic oxygen furnace
Specifications
MgO and carbon content range from 84% to 90%
Widely used throughout metallurgical industry
Physical And Chemical Indicators
STEEL LADLE |
|||||||||
Brand |
Chemical Properties (%) |
Physical Properties |
Main Application |
||||||
MgO |
FC |
Al2O3 |
AP (%) |
BD (g/cm3) |
CCS (MPa) |
HMOR (1400ºCX0.5hr) |
|||
LF 8 BI |
90 |
8 |
2 |
4 |
3 |
45 |
8 |
Bottom Impact |
|
LF 8 BN |
90 |
8 |
2 |
4 |
3 |
45 |
6 |
Bottom Non Impact |
|
LF 10 BC |
88 |
10 |
2 |
4 |
3 |
45 |
8 |
Bottom Conical/Splash Pad |
|
LF 12 MP |
86 |
12 |
2 |
4 |
3.05 |
45 |
10 |
Metal Zone Purging |
|
LF 12 MN |
86 |
12 |
2 |
5 |
3.05 |
40 |
6 |
Metal Zone Non Purging |
|
LF 14 SP |
84 |
14 |
2 |
3 |
3.1 |
40 |
10 |
Slag Zone Purging |
|
LF 14 SN |
84 |
14 |
2 |
3 |
3.1 |
40 |
8 |
Slag Zone Non Purging |
|
LF 13 FB |
85 |
13 |
2 |
5 |
3 |
40 |
6 |
Free Board |
Semi-silica brick refers to an aluminum-silicon refractory product with a SiO2 content of greater than 65% and an Al2O3 content of 15% to 30%. They generally use clay containing quartz impurities or native kaolin refractory clay or tailings and pyroph...
The Al2O3 content of anchor bricks is above 55%, and some users require that the alumina content reach 75%, and the load softening temperature of 75% bricks reaches 1550C. However, in actual use, anchor bricks with high aluminum content cannot be enough. The key is Flexibility is the most important t...
Products Desc
Products Description The main components of alkali resistant bricks are clay, high alumina, quartz sand, bauxite and other alkali resistant materials, among which quartz sand and bauxite can improve alkali resistance, clay and high alumina can increase sintering pressure, so that alkali-resistant bri...
Professional solutions for you, ready for your choice
Copyright © Zibo Lifa Refractory Materials Factory ALL RIGHTS RESERVED
Technical Support: JinZhao E-commerce