Ceramic roller is made of high-purity alumina as the main raw material. After high-temperature firing, it has the characteristics of high temperature resistance, corrosion resistance, good thermal conductivity, oxidation resistance, no deformation and no shrinkage. Widely used in furnaces, annealing furnaces, tempering furnaces, glass furnaces, electric furnace products, non-ferrous metal smelting, zinc and aluminum plants and other industries.
Keywords:
Category:
Industrial Ceramic
E-mail:
154872569@qq.com
Ceramic Roller Details
Product Description
Ceramic roller is made of high-purity alumina as the main raw material. After high-temperature firing, it has the characteristics of high temperature resistance, corrosion resistance, good thermal conductivity, oxidation resistance, no deformation and no shrinkage. It can effectively prevent high temperature solutions from heating elements (silicon carbon rods, electric furnaces) Wire) erosion, greatly improving product life. Widely used in ceramic roller furnaces, annealing furnaces, tempering furnaces, glass furnaces, electric furnace products, non-ferrous metal smelting, zinc and aluminum plants and other industries.
Ceramic rollers are the most critical refractory materials in roller kilns, which play the role of carrying and transferring products in the kiln. With the development of ceramic production and the wide application of roller kilns in building sanitary ceramics, daily-use porcelain and special ceramics, the requirements for refractory materials used in kilns are constantly increasing, especially the strength and High temperature mechanical properties put forward newer requirements. It is the development trend of domestic and foreign, because it fully meets the various needs of wall and floor tile production, and has the advantages that others cannot.
This project is a key component of modern industrial rail kilns and can drive and carry ceramic products at high temperatures up to 1400°C.
They are the most mature engineering ceramics, with excellent electrical insulation properties, high hardness and good wear resistance, but relatively low strength and fracture toughness.
New formula and process, with super thermal shock resistance, higher high-temperature strength and high-temperature bearing capacity, most suitable for ultra-wide body kilns, such as firing large polished tiles, glazed tiles, roof tiles And heavy load products, high-volume production environment roller kiln.
Features
High hardness
Good heat resistance and wear resistance
Strong corrosion resistance
Strong thermal shock stability
Application
Petroleum industry, chemical industry, precision machinery, etc.
Physical And Chemical Indicators
Technical index |
JUCOS-A |
JUCOS-B |
JUCOS-C |
alumina content |
80-82% |
78-80% |
76-78% |
Bending strength |
60-70 Mpa |
50-60Mpa |
40-50 Mpa |
Bulk density |
2.7-2.9g/cm3 |
2.55-2.7g/cm3 |
2.5-2.6g/cm3 |
Max service temperature |
1350 |
1300 |
1250 |
water absorption |
5-7 |
6-8% |
7-9% |
Pictures
Semi-silica brick refers to an aluminum-silicon refractory product with a SiO2 content of greater than 65% and an Al2O3 content of 15% to 30%. They generally use clay containing quartz impurities or native kaolin refractory clay or tailings and pyroph...
The Al2O3 content of anchor bricks is above 55%, and some users require that the alumina content reach 75%, and the load softening temperature of 75% bricks reaches 1550C. However, in actual use, anchor bricks with high aluminum content cannot be enough. The key is Flexibility is the most important t...
Products Desc
Products Description The main components of alkali resistant bricks are clay, high alumina, quartz sand, bauxite and other alkali resistant materials, among which quartz sand and bauxite can improve alkali resistance, clay and high alumina can increase sintering pressure, so that alkali-resistant bri...
Professional solutions for you, ready for your choice