The raw material of magnesium brick production mainly relies on magnesite. The production process of magnesia brick is to mix dead burned magnesia (particles below 5 mm to fine powder) with an appropriate amount of sulfite pulp waste liquid or caustic magnesia as the binder under the press molding. Magnesium brick components are: metallurgical magnesia , sulfite pulp waste liquid, caustic magnesia. Advantages High temperature resistance Resistance to alkaline slag erosion ability is strong Multi mineral composition, strong alkalinity, high density Magnesium brick has good thermal conductivity a
Keywords:
Category:
Shape Refractory
E-mail:
154872569@qq.com
Magnesium Brick Details
The raw material of magnesium brick production mainly relies on magnesite. The production process of magnesia brick is to mix dead burned magnesia (particles below 5 mm to fine powder) with an appropriate amount of sulfite pulp waste liquid or caustic magnesia as the binder under the press molding. Magnesium brick components are: metallurgical magnesia, sulfite pulp waste liquid, caustic magnesia.
Advantages
High temperature resistance
Resistance to alkaline slag erosion ability is strong
Multi mineral composition, strong alkalinity, high density
Magnesium brick has good thermal conductivity and low thermal insulation
Precautions
High thermal conductivity, second only to carbon brick and silicon carbide brick in refractory products
The thermal shock resistance is poor, so the purity of magnesium brick can improve the thermal shock resistance
The ability to resist acid slag is very poor. It can not be directly contacted with silicon brick when used. Generally, it should be separated by neutral brick
Hydration resistance is poor, water is easy to hydrate, and produce cracks, reduce its strength. Therefore, in the storage and transportation should pay attention to moisture, rain and snow
Application
Magnesium brick can withstand high temperature heat load of liquid steel and molten slag, flow scouring of fluid and chemical erosion of liquid steel and strong alkaline slag, so it is widely used in high temperature industries such as steel, metallurgy, glass and cement
Physical And Chemical Indicators
Brand Properties |
MD92 |
MD95 |
MD97 |
MD98 |
|
Bulk density(g/cm3) |
2.90 |
2.95 |
3.00 |
3.00 |
|
Refractoriness under load T2 (ºC) |
1550 |
1650 |
1700 |
1700 |
|
Apparent Porosity (%) |
18 |
16 |
15 |
15 |
|
Cold Crushing Strength(MPa) |
55 |
60 |
70 |
80 |
|
Thermal shock resistance 950deg air cool (times) |
10 |
10 |
10 |
10 |
|
Composition(%) |
MGO |
92 |
95 |
97 |
97.5 |
CaO |
2.5 |
2.0 |
1.6 |
1.2 |
|
SiO2 |
3.5 |
2.5 |
1.2 |
0.6 |
Welcome to contact us!
Semi-silica brick refers to an aluminum-silicon refractory product with a SiO2 content of greater than 65% and an Al2O3 content of 15% to 30%. They generally use clay containing quartz impurities or native kaolin refractory clay or tailings and pyroph...
The Al2O3 content of anchor bricks is above 55%, and some users require that the alumina content reach 75%, and the load softening temperature of 75% bricks reaches 1550C. However, in actual use, anchor bricks with high aluminum content cannot be enough. The key is Flexibility is the most important t...
Products Desc
Products Description The main components of alkali resistant bricks are clay, high alumina, quartz sand, bauxite and other alkali resistant materials, among which quartz sand and bauxite can improve alkali resistance, clay and high alumina can increase sintering pressure, so that alkali-resistant bri...
Professional solutions for you, ready for your choice
Copyright © Zibo Lifa Refractory Materials Factory ALL RIGHTS RESERVED
Technical Support: JinZhao E-commerce