Making Process of Magnesia Iron Spinel Bricks: The key raw materials magnesia and iron-spinel are carefully selected and processed to meet specific quality and purity requirements. The raw materials are thoroughly mixed to form a homogeneous mixture for use in forming bricks. Depending on the specific application and manufacturing process, the mixture is shaped into the desired brick shape using various techniques such as pressing, extrusion or casting. Features 1.High Temperature Resistance:They can withstand temperatures well above 1,700C (3,092F) without significant deformation or degradatio
Keywords:
Category:
Shape Refractory
E-mail:
154872569@qq.com
Magnesia Iron Spinel Brick Details
Making Process of Magnesia Iron Spinel Bricks: The key raw materials magnesia and iron-spinel are carefully selected and processed to meet specific quality and purity requirements. The raw materials are thoroughly mixed to form a homogeneous mixture for use in forming bricks. Depending on the specific application and manufacturing process, the mixture is shaped into the desired brick shape using various techniques such as pressing, extrusion or casting.
1.High Temperature Resistance:They can withstand temperatures well above 1,700°C (3,092°F) without significant deformation or degradation.
2.Chemical Corrosion Resistance:They can withstand exposure to molten metals, corrosive slags, and various chemical compounds.
3. Their ability to maintain their structural integrity and refractory properties over extended periods of use reduces the frequency of replacements and maintenance.
Brand & Properties | MH brick |
Bulk Density (g/cm3) |
2.95 |
Cold Crushing Strength (MPa) | 45 |
Apparent Porosity(%) | 18 |
Thermal Shock Resistance at 1,100℃ Water cooling | 8 |
Refractoriness under Load (0.2MPa,T2℃) | 1680 |
1.Steel industry:
- Ladle: They are used to arrange ladle used for transporting and pouring molten steel.
Electric arc Furnace (EAF) : magnesium-iron spinel bricks are used to line the walls and roofs of electric arc furnaces, which are essential for secondary steelmaking.
2.Cement industry:
- Rotary kilns: They are used in lined rotary kilns used in cement production, where the clinker manufacturing process requires high temperature resistance.
3.Glass manufacturing:
- Glass furnaces: magnesia spinel bricks are used to line glass furnaces.
- Heat accumulators: They are used in lining heat accumulators, which are components in glass furnaces that help control and optimize temperature.
4.Non-ferrous metal industry:
Copper and aluminum smelting: These bricks are used to line various equipment in the smelting process of non-ferrous metals.
Semi-silica brick refers to an aluminum-silicon refractory product with a SiO2 content of greater than 65% and an Al2O3 content of 15% to 30%. They generally use clay containing quartz impurities or native kaolin refractory clay or tailings and pyroph...
The Al2O3 content of anchor bricks is above 55%, and some users require that the alumina content reach 75%, and the load softening temperature of 75% bricks reaches 1550C. However, in actual use, anchor bricks with high aluminum content cannot be enough. The key is Flexibility is the most important t...
Products Desc
Products Description The main components of alkali resistant bricks are clay, high alumina, quartz sand, bauxite and other alkali resistant materials, among which quartz sand and bauxite can improve alkali resistance, clay and high alumina can increase sintering pressure, so that alkali-resistant bri...
Professional solutions for you, ready for your choice
Copyright © Zibo Lifa Refractory Materials Factory ALL RIGHTS RESERVED
Technical Support: JinZhao E-commerce