Magnesia Chrome Brick is characterized by a high direct bonding rate and large crystals. It has good resistance to heat flaking. Low alkali neutrality has good slag resistance when repairing low acid feed furnaces. The main raw materials for manufactu
Keywords:
Category:
Shape Refractory
E-mail:
154872569@qq.com
Magnesia Chrome Brick Details
Magnesia Chrome Brick is characterized by a high direct bonding rate and large crystals. It has good resistance to heat flaking. Low alkali neutrality has good slag resistance when repairing low acid feed furnaces. The main raw materials for manufacturing magnesia-chrome bricks are sintered magnesium and chromite. The purity of the magnesium oxide raw material should be as high as possible. The chemical composition requirements of chromite are: Cr 2 O 3: 30-45%, CaO: ≤1.0-1.5%.
Features
Magnesia Chrome Brick has the following characteristics:
Good thermal shock resistance
Excellent slag wear resistance
Good cold compression strength
High temperature resistance and high fire resistance
High-grade chrome ore raw materials
Lower impurity content
Applications
Magnesia Chrome Brick is mainly used in the metallurgical industry, such as the construction of flat-bottom furnace roofs, electric furnace roofs, refining furnaces outside the furnace, and various non-ferrous metal smelting furnaces. The high-temperature part of the wall of the ultra-high power electric furnace is made of fused cast magnesia-chrome bricks, and the high-corrosion area of the external refining furnace is made of synthetic materials. In addition, magnesia-chrome bricks are also used in the cement rotary kiln firing zone and glass kiln regenerators.
Specifications
Brand Properties |
RMC-22 |
RMC-16 |
RMC-12 |
DMC-22 |
DMC-16 |
DMC-8 |
|
Apparent Porosity (%) |
15 |
15 |
15 |
16 |
17 |
18 |
|
Bulk Density (g/cm3) |
3.25 |
3.20 |
3.20 |
3.15 |
3.0 |
2.95 |
|
Cold Crushing Strength (MPa) |
50 |
50 |
50 |
40 |
40 |
40 |
|
@ 1400℃ Thermal Linear Expansion(%) |
1.8 |
1.5 |
1.2 |
1.8 |
1.5 |
1.2 |
|
950℃ (times)Thermal Shock Resistance air cool |
60 |
55 |
50 |
40 |
40 |
40 |
|
@0.2MPa Refractoriness Under Load (℃) |
1700 |
1700 |
1700 |
1700 |
1650 |
1600 |
|
Chemical Composition (%) |
MgO |
55 |
65 |
75 |
55 |
65 |
75 |
Cr2O3 |
22 |
16 |
12 |
22 |
16 |
8 |
|
SiO2 |
1.5 |
1.5 |
1.5 |
2.0 |
2.0 |
2.5 |
|
Main Applications |
Rotary & Shaft Kiln |
Semi-silica brick refers to an aluminum-silicon refractory product with a SiO2 content of greater than 65% and an Al2O3 content of 15% to 30%. They generally use clay containing quartz impurities or native kaolin refractory clay or tailings and pyroph...
The Al2O3 content of anchor bricks is above 55%, and some users require that the alumina content reach 75%, and the load softening temperature of 75% bricks reaches 1550C. However, in actual use, anchor bricks with high aluminum content cannot be enough. The key is Flexibility is the most important t...
Products Desc
Products Description The main components of alkali resistant bricks are clay, high alumina, quartz sand, bauxite and other alkali resistant materials, among which quartz sand and bauxite can improve alkali resistance, clay and high alumina can increase sintering pressure, so that alkali-resistant bri...
Professional solutions for you, ready for your choice
Copyright © Zibo Lifa Refractory Materials Factory ALL RIGHTS RESERVED
Technical Support: JinZhao E-commerce