The refractory temperature of the clay cast block is 1580~1770(C), the product category is refractory brick, the material is kaolin, the thermal conductivity (normal temperature) is 0.035, the grade is a class fireproof, the low temperature bending is less than or equal to the national standard, and the elongation at break is The rate is the national standard, the flexural strength is the national standard, the compressive strength is the national standard, the tensile strength is the national standard, the service temperature is 1500C, the tear strength is the national standard, the core mater
Keywords:
Category:
Shape Refractory
E-mail:
154872569@qq.com
Cast Blocks Details
The refractory temperature of the clay cast block is 1580~1770(°C), the product category is refractory brick, the material is kaolin, the thermal conductivity (normal temperature) is 0.035, the grade is a class fireproof, the low temperature bending is less than or equal to the national standard, and the elongation at break is The rate is the national standard, the flexural strength is the national standard, the compressive strength is the national standard, the tensile strength is the national standard, the service temperature is 1500°C, the tear strength is the national standard, the core material is a grade clay, the shape is solid, the shape is a rectangle, Specifications are standard specifications (mm)
Feature
Our company adopts a high-power vibration platform, which is suitable for the vibration molding process of special refractory castables to produce large clay bricks for the bottom of glass furnaces. Its physical and chemical indicators and product appearance are superior to other similar products. Its main feature is that it is far superior to the products formed by the traditional slurry casting process or the ramming process in the corrosion resistance of the glass liquid.
Application
The products are mainly used for float glass, lattice glass, bottle and jar glass, glass fiber, pharmaceutical glass, daily-use glass, furnace bottom of craft glass kiln, flaming port, 1 port for feeding, pool wall, etc. Kaolin clay cast block need to be poured according to the drawings. It is mainly used for glass kilns and the bottom construction of caustic soda boilers. It has the advantages of high temperature resistance and no deformation. It can bring convenience to the construction of kilns. It is a special brick required for various kilns. Indispensable building material.
Physical And Chemical Indicators
Products Properties |
Cast blocks |
CCAS | |
Al₂O₃(%) | 45 |
SiO₂(%) | 53 |
Fe₂O3(%) | 1.2 |
Apparent Porosity(%) | 19 |
Bulk Density(g/cm³) | 2.3 |
MpaCold Crushing Strength(MPa) | 70 |
Refractoriness under load(℃) | 1500 |
Semi-silica brick refers to an aluminum-silicon refractory product with a SiO2 content of greater than 65% and an Al2O3 content of 15% to 30%. They generally use clay containing quartz impurities or native kaolin refractory clay or tailings and pyroph...
The Al2O3 content of anchor bricks is above 55%, and some users require that the alumina content reach 75%, and the load softening temperature of 75% bricks reaches 1550C. However, in actual use, anchor bricks with high aluminum content cannot be enough. The key is Flexibility is the most important t...
Products Desc
Products Description The main components of alkali resistant bricks are clay, high alumina, quartz sand, bauxite and other alkali resistant materials, among which quartz sand and bauxite can improve alkali resistance, clay and high alumina can increase sintering pressure, so that alkali-resistant bri...
Professional solutions for you, ready for your choice
Copyright © Zibo Lifa Refractory Materials Factory ALL RIGHTS RESERVED
Technical Support: JinZhao E-commerce