Products Description The steel fiber used to make refractory castables generally has a diameter of 0.4-0.5mm and a length of 25mm. The shape and cross-section of the steel fiber are crescent-shaped. The amount of steel fiber added to the castable is 1-5% (weight), and the length and amount of steel fiber should be appropriate. Generally, water is added to the mixture first, and then steel fiber is added for full stirring. It not only makes the mixture evenly stirred, but also saves 1/3 of the stirring time compared with stirring in the dry material where the steel fiber is placed. The molding c
Keywords:
Category:
Monolithic Refractory
E-mail:
154872569@qq.com
Steel Fiber Castable Details
The steel fiber used to make refractory castables generally has a diameter of 0.4-0.5mm and a length of 25mm. The shape and cross-section of the steel fiber are crescent-shaped. The amount of steel fiber added to the castable is 1-5% (weight), and the length and amount of steel fiber should be appropriate.
Generally, water is added to the mixture first, and then steel fiber is added for full stirring. It not only makes the mixture evenly stirred, but also saves 1/3 of the stirring time compared with stirring in the dry material where the steel fiber is placed. The molding can be vibrated externally, or vibrated inside the mixture with a vibrating rod, and dense products can also be obtained.
1.The steel fiber strengthens the tensile and bending strength of the refractory castable.
2. Steel fibers can improve the thermal shock resistance of castables.
3. The steel fiber refractory castable can still carry the load even after cracking, thus improving the fracture work of the castable and increasing the plasticity of the refractory castable.
4. Steel fiber castable can improve the mechanical strength after heat treatment.
1. The lining layer of various thermal equipment.
2. Flue, heat insulation inside large diameter metal chimney.
3. Industrial boiler lining, the effect is more obvious when used on the furnace top.
4. Low-temperature air (≤1200°C) heat insulation in the pipeline.
5. KT-J anti-carburizing fiber castable is used for muffle-free carburizing furnace lining.
6. Various common and special-shaped prefabricated parts can meet the special application requirements of users.
7. The backing insulation layer (including the furnace wall and furnace roof) of various low-temperature furnaces and kilns with an interface temperature of ≤1050°C.
8. For industrial furnaces using flat flame burners, the top of the furnace is sealed and insulated, and the sealing effect is better than any other materials.
9. For the lining of resistance furnace with working temperature ≤1200℃, the electric heating element can be exposed or embedded.
10. There is no mechanical vibration during the work, and it is especially suitable for furnace linings with large temperature changes, such as bell furnaces, movable furnace covers of removable aluminum melting furnaces, etc.
Semi-silica brick refers to an aluminum-silicon refractory product with a SiO2 content of greater than 65% and an Al2O3 content of 15% to 30%. They generally use clay containing quartz impurities or native kaolin refractory clay or tailings and pyroph...
The Al2O3 content of anchor bricks is above 55%, and some users require that the alumina content reach 75%, and the load softening temperature of 75% bricks reaches 1550C. However, in actual use, anchor bricks with high aluminum content cannot be enough. The key is Flexibility is the most important t...
Products Desc
Products Description The main components of alkali resistant bricks are clay, high alumina, quartz sand, bauxite and other alkali resistant materials, among which quartz sand and bauxite can improve alkali resistance, clay and high alumina can increase sintering pressure, so that alkali-resistant bri...
Professional solutions for you, ready for your choice
Copyright © Zibo Lifa Refractory Materials Factory ALL RIGHTS RESERVED
Technical Support: JinZhao E-commerce