Ceramic fiber cloth is made of ceramic fiber plus organic fiber, lined with glass fiber (steel wire), and then woven into cloth. It is a new type of inorganic thermal insulation, fire-resistant village material, with light weight, small heat capacity, good thermal insulation performance and high temperature insulation performance, stable chemical properties, etc. Ceramic fiber cloth was invented afterwards, completely replacing asbestos cloth. Asbestos cloth has carcinogenic effect, and the strength of ceramic fiber cloth is also better. Construction environment: 1. Require the mixed slurry t
Keywords:
Category:
Insulation Thermal Material
E-mail:
154872569@qq.com
Ceramic Fiber Cloth Details
Ceramic fiber cloth is made of ceramic fiber plus organic fiber, lined with glass fiber (steel wire), and then woven into cloth. It is a new type of inorganic thermal insulation, fire-resistant village material, with light weight, small heat capacity, good thermal insulation performance and high temperature insulation performance, stable chemical properties, etc.
Ceramic fiber cloth was invented afterwards, completely replacing asbestos cloth. Asbestos cloth has carcinogenic effect, and the strength of ceramic fiber cloth is also better.
Construction environment:
1. Require the mixed slurry to mature after 15-25 minutes to ensure that the slurry reaches the best construction viscosity.
2. It is required to determine the amount of paint to be prepared according to the construction capacity, and it can be used as needed. The prepared coating should be used up within 120 minutes, and cannot be used again after setting.
3. It is recommended to apply the spraying method for construction. The thickness of the coating is not more than 5 mm. The second pass can be sprayed or smeared. The thickness of the coating should not exceed 10 mm per pass. The interval between each pass is 24 hours until it reaches The design thickness is not less than 13.3 mm.
4. The ambient temperature of the construction site is required to be 5-38℃, and the relative humidity is not more than 85%. The curing period of physical and chemical performance inspection is 28 days, and the curing period of refractory performance inspection is 40 days.
5. If the paint is applied outdoors, after the coating is basically dried, the surface of the fire retardant paint must be coated with acid-proof and alkali-modified acrylic paint to protect it.
6. Undried coatings must not be bumped, washed by water or rain.
Features
1. Low thermal shock coefficient and low heat capacity;
2. Good high temperature insulation performance and long service life;
3. Has the ability to resist non-ferrous metals such as aluminum and zinc, etc.
4. Has good low temperature and high temperature strength;
Application
1. Insulation of various kilns, high-temperature pipes and containers;
2. Furnace door, valve, flange seal, fire door and fire shutter material, high temperature furnace door sensitive curtain;
3. Insulation of engine and instrument, fireproof cable coating material, high temperature fireproof material;
4. Insulation covering fabric, high-temperature expansion joint filler, and flue lining;
5. Labor insurance products, fireproof clothing, high-temperature filtration, sound absorption and other applications to replace asbestos.
Semi-silica brick refers to an aluminum-silicon refractory product with a SiO2 content of greater than 65% and an Al2O3 content of 15% to 30%. They generally use clay containing quartz impurities or native kaolin refractory clay or tailings and pyroph...
The Al2O3 content of anchor bricks is above 55%, and some users require that the alumina content reach 75%, and the load softening temperature of 75% bricks reaches 1550C. However, in actual use, anchor bricks with high aluminum content cannot be enough. The key is Flexibility is the most important t...
Products Desc
Products Description The main components of alkali resistant bricks are clay, high alumina, quartz sand, bauxite and other alkali resistant materials, among which quartz sand and bauxite can improve alkali resistance, clay and high alumina can increase sintering pressure, so that alkali-resistant bri...
Professional solutions for you, ready for your choice
Copyright © Zibo Lifa Refractory Materials Factory ALL RIGHTS RESERVED
Technical Support: JinZhao E-commerce