Soluble fiber blanket is body soluble fiber that utilizing a unique spinning technology and mechanical properties. These special fibers are made from a blend or calcium,silica and magnesium which give fiber the ability to support continuous application under high temperature conditions. Soluble fiber blanket is flexible and competent in treating with the refractory linings, thermal insulation and metals transfer, it has been Proven superior and eco-friendly to traditional refractory ceramic fiber. Soluble fiber blanket is alkaline earth silicate fiber with SiO2, MgO and CaO as main components.
Keywords:
Category:
Insulation Thermal Material
E-mail:
154872569@qq.com
Soluble Fiber Blanket Details
Soluble fiber blanket is body soluble fiber that utilizing a unique spinning technology and mechanical properties. These special fibers are made from a blend or calcium,silica and magnesium which give fiber the ability to support continuous application under high temperature conditions. Soluble fiber blanket is flexible and competent in treating with the refractory linings, thermal insulation and metals transfer, it has been Proven superior and eco-friendly to traditional refractory ceramic fiber.
Soluble fiber blanket is alkaline earth silicate fiber with SiO2, MgO and CaO as main components. Because it has a certain solubility in human body fluids and reduces damage to human health, it is called soluble fiber.
Due to the introduction of MgO, CaO and other components, it is helpful to expand the viscosity range of fiber formation, improve fiber formation conditions, and improve fiber formation rate and fiber flexibility. However, due to the introduction of components such as MgO and CaO, low-melting compounds such as CaO·SiO2, CaO·Mgo·2SiO2, etc. are formed, which causes a decrease in the heat resistance of the fiber. Therefore, generally soluble fibers belong to low-grade ceramic fibers, and their products are mostly used as backing materials for industrial kilns. In order to improve the heat resistance of soluble fibers, the method of attracting zrO2 components is adopted to increase the viscosity of the glass phase, inhibit the growth rate of the crystal grains after the fiber is heated and crystallized, and improve the heat resistance of soluble fibers.
Features
Low thermal conductivity
Low heat storage
High tensile strength
Thermal shock resistance
Light weight
Applications
Back-up insulation for dense refractory
Annealing furnace linings
Stress relieving blanket
Heat treatment furnace linings
Crude heater linings
Physical And Chemical Indicators
Brand Properties |
Soluble Fiber Blanket |
|||||
Specification Temp. (℃) |
1100 |
1300 |
||||
Bulk Density (kg/m3) |
64 |
96 |
128 |
96 |
128 |
|
(%)@24 Linear Shrinkage after Heating |
1100℃x24h≤1.0 |
1260℃x24h≤3.0 |
||||
Tensile strength (MPa) |
0.03 |
0.05 |
0.07 |
0.05 |
0.07 |
|
Shot content (%) |
≤12 |
≤12 |
||||
Thermal Conductivity (w/m.k) |
200℃ |
0.06 |
0.05 |
0.05 |
0.05 |
0.04 |
400℃ |
0.11 |
0.09 |
0.08 |
0.10 |
0.08 |
|
600℃ |
0.17 |
0.13 |
0.12 |
0.18 |
0.14 |
|
800℃ |
0.28 |
0.20 |
0.17 |
0.30 |
0.22 |
|
1000℃ |
0.40 |
0.28 |
0.25 |
0.46 |
0.33 |
|
1200℃ |
- |
- |
- |
0.68 |
0.46 |
|
Chemical Composition (%) |
SiO2 |
62-68 |
≥70 |
|||
CaO |
26-32 |
- |
||||
MgO |
4-7 |
- |
||||
CaO+MgO |
- |
≥20 |
||||
Size(mm) |
LENGTH*WIDTH*THICKNESS 7200*610/1220*25,3600*610/1220*50,4800*610/1220*38 7200*610/1220*6,14400*610/1220*12.5,28800*610/1220*6.38 |
Semi-silica brick refers to an aluminum-silicon refractory product with a SiO2 content of greater than 65% and an Al2O3 content of 15% to 30%. They generally use clay containing quartz impurities or native kaolin refractory clay or tailings and pyroph...
The Al2O3 content of anchor bricks is above 55%, and some users require that the alumina content reach 75%, and the load softening temperature of 75% bricks reaches 1550C. However, in actual use, anchor bricks with high aluminum content cannot be enough. The key is Flexibility is the most important t...
Products Desc
Products Description The main components of alkali resistant bricks are clay, high alumina, quartz sand, bauxite and other alkali resistant materials, among which quartz sand and bauxite can improve alkali resistance, clay and high alumina can increase sintering pressure, so that alkali-resistant bri...
Professional solutions for you, ready for your choice
Copyright © Zibo Lifa Refractory Materials Factory ALL RIGHTS RESERVED
Technical Support: JinZhao E-commerce